Fosroc Renderoc RSXtra Repair (Formerly Renderoc RS)
Rapid setting. polymer modified, repair concrete

    This combination does not exist.

    Submit

      Terms and Conditions
    - Prices excluding delivery costs.
    - The above price may vary depending on the availability of raw material price, delivery and minimum order quantity.

            

    Fosroc Concrete Repair

    Related Blogs

    Fosroc, Constructive Solutions

    TDS


    Renderoc RSXtra is a blend of dry powders and graded aggregates which requires only the site addition of clean water to produce a highly consistent, high strength, free flowing repair concrete which self-compacts. 
    Renderoc RSXtra exhibits excellent thermal compatibility with concrete and good water repellent properties.

    Your Dynamic Snippet will be displayed here... This message is displayed because you did not provided both a filter and a template to use.
    • Cost Effective - pioneering ‘DS Technology’ ensures shrinkage control, and enables repairs to be completed ‘right first time’
    • Rapid strength gain - accepts vehicular traffic in 2 hrs
    • Good durability - high strength, abrasion and weather resistance
    • Economical - can be ‘bulked-out’ with graded aggregate in some locations
    • Self compacting - eliminates honeycombing voids

    For the emergency reinstatement of damaged or deteriorated concrete. The material can be used internally or externally and is particularly suitable for repairs to:

    • Airport runways and aprons
    • Areas where wheeled traffic requires fast return to service

    Where shown on the contract documents, the fast setting repair concrete shall be Renderoc RSXtra; a single component, cement-based blend of powders and graded aggregates, to which only the site-addition of water shall be permitted. 

    The cured repair shall achieve compressive strengths of 
    15 N/mm2after 3 hours
     30 N/mm2after 1 day 
    45 N/mm2after 28 days (at 25oC). 

    The material shallthus be capable of supporting pedestrian and vehicular traffic after 4 hours, at an ambient temperature of 25oC.